Stryker?(TMZF?)


UNS R58120


Product Specifications By Form

Bar

Metallurgical Condition 1,400 °F anneal. 0.2% Yield Strength. Reduction in Area, 40%.

Composition

ElementMinimum (weight %)Maximum (weight %)Typical (weight %)
H 0.02 
C 0.02 
Mo12.0  
Zr6.0  
Fe2.0  
O0.18  
N0.01  
TiBalance  

Density

lb/in3g/cm3
0.1804.98

Tensile Strength

ksiMPa
145 min1000 min

Yield Strength

ksiMPa
140 min965 min

Hardness

33 HRC max

Elongation

15% min
Billet

Metallurgical Condition 1,400 °F anneal. 0.2% Yield Strength. Reduction in Area, 40%.

Composition

ElementMinimum (weight %)Maximum (weight %)Typical (weight %)
H 0.02 
C 0.02 
Mo12.0  
Zr6.0  
Fe2.0  
O0.18  
N0.01  
TiBalance  

Density

lb/in3g/cm3
0.1804.98

Tensile Strength

ksiMPa
145 min1000 min

Yield Strength

ksiMPa
140 min965 min

Hardness

33 HRC max

Elongation

15% min